  • 杭州伟国型钢有限公司 抛丸机配件
  • 本站编辑:杭州伟国型钢有限公司发布日期:2019-05-03 14:10 浏览次数:
优质的抛丸机配件是整台机械的核心,能保证设备长期以最低成本运行。。 
     叶片:抛丸机叶片采用简便的定向凝固铸造工艺和改进的热处理工艺使碳化物垂直于磨面定向排列,降低残余奥氏体数量,消除了收缩缺陷,提高了致密度,使用寿命可达到1000小时以上。所有的叶片铸造后均经过严格地修整打磨,通过天平称重配对,因此其偏向冲击很小,每个叶片重量差≤5g。 
      定向套:全封闭刻度盘式,可方便地调节抛射角度和抛出方向,选用高铬特种耐磨铸铁制抛丸机配件成,每批配件均经过外型检测,和材质检测。
     清理室护板:轧制Mn13护板对弹丸的强冲击磨损和大应力磨损有极好的耐磨性能,外来冲击越大,其自身表层耐磨性越高,在较大冲击或较大接触应力的作用下,高锰钢板表层会产生加工硬化,表面硬度由HB200迅速提升到HB500以上,从而产生高耐磨的表面层,而钢板内层奥氏
体仍保持良好的冲击韧性。并且随着表面硬化层的逐渐磨损,新的加工硬化层会连续不断形成,使用中不会出现破碎。使用寿命可达到8年以上。

The high quality pellet machine accessories are the core of the entire machine, which can ensure that the equipment can be operated at the lowest cost for a long time. And ...
Blade: The blade of the pellet machine adopts a simple directional solidification casting technology and an improved heat treatment technology to make the carbides perpendicular to the orientation of the abrasive surface, reduce the number of residual austenitic bodies, eliminate shrinkage defects, and increase the density. The service life can reach 1000 hours or more. After all the leaves are cast, they are strictly trimmed and polished, and they are weighted and paired by the balance, so their bias impact is very small, and the weight difference of each blade ≤ 5G.
Directional sleeve: fully closed dial type, which can easily adjust the throwing angle and throw direction, selected high-chromium special molded iron casting machine accessories, each batch of accessories have undergone external detection, and material testing.
Cleaning room protection: Rolling Mn13 protection plate has excellent wear resistance to the strong impact wear and large stress wear of the projectile. The greater the external impact, the higher the wear resistance of its own surface surface, under the action of larger impact or larger contact stress. The surface of the high-manganese steel plate will produce processing hardening, and the surface hardness will be rapidly increased from HB200 to HB500 or more, resulting in a highly wearable surface layer, while the inner layer of the steel plate is Austenitic.
The body still maintains good impact toughness. And with the gradual wear of the surface hardening layer, the new processing hardening layer will continue to form, and there will be no fragmentation during use. The useful life can reach more than 8 years.